1·The main cause of the cracking is that the quenching temperature is too high.
结果表明,钢球开裂为淬火开裂,淬火温度过高是导致淬火钢球开裂的主要原因。
2·The results show that the higher the second quenching temperature, the higher the hardness.
结果表明,随二次淬火温度的升高,硬度逐渐升高。
3·The embrittlement of the welds increases with the increase of quenching temperature of PWHT.
淬火温度越高,焊缝脆化越严重;
4·The Influence of quenching temperature on wear resistance of high boron casting steel was investigated.
研究了不同的淬火温度对高硼铸钢冲击耐磨性的影响。
5·The effects of polymer molecular weight and quenching temperature on the porous structure are also discussed.
讨论了聚合物分子量及淬冷温度对成膜孔结构的影响。
6·The hardness and impact toughness increase at first and then drop down with the increases of quenching temperature.
随奥氏体化温度的升高,实验钢的硬度和冲击韧度先升高后降低;
7·On the other hand, the parts might become more brittle at higher quenching temperature because of the coarse martensite.
若淬火温度较高,由于粗大马氏体的存在,脆性很大;
8·The influences of isothermal quenching temperature on the retained austenite and mechanical properties of ADI were studied.
研究了等温淬火温度对ADI中残余奥氏体及其力学性能的影响。
9·The result indicates that under different quenching temperature and holding time, the formed bainite morphology are different.
结果表明,在不同淬火温度和保温时间下形成不同的贝氏体形貌。
10·It is shown by the results that the morphology of microstructure is dependent on the interrupted quenching temperature strongly.
结果表明,微观组织形态取决于水淬终止温度。