1·Chemical oxidation: through the chemical processing the metal surface oxidation film formation process.
化学氧化:通过化学处理使金属表面形成氧化膜的过程。
2·Must do derusting and to oxidation film processing, generally use chemical polishing or electrolytic polishing.
必须先做除锈及去氧化膜处理,一般使用化学抛光或电解抛光。
3·Peeling of oxidation film and oxidation-decarbonization are more serious on the surface than on the sub-surface.
试样表面的氧化腐蚀及氧化皮剥落均比次表层严重,表面的开裂也加速了次表层裂纹的形核和扩展。
4·Structure, composition and corrosion resistance of the anodic oxidation film on the magnesium alloy surface were discussed.
在硫酸电解液中加入适量由羧酸和有机化合物组成的添加剂 ,制得铝合金阳极氧化膜。
5·In the first stage of anodic deposition, the flocculent oxidation film deposits and extends on the surface of magnesium alloy.
阳极沉积阶段是在阳极表面形成团絮状的沉积氧化膜及氧化膜不断扩展的过程;
6·The effects of anodic oxidation process on thickness, corrosion resistance and surface morphology of hard oxidation film were studied.
为了研究阳极氧化工艺条件对硬质氧化膜的厚度、耐蚀性、表面形貌的影响。
7·According to the requirement of the mechanical properties and oxidation film of 6063 alloy, the best plan of alloy component is presented.
根据对6063合金力学性能和氧化膜的要求,提出了最佳的合金成分方案。
8·The heated oxidation film of U-Nb alloy is studied by auger electron spectroscopy (AES) at different temperature in the high vacuum chamber.
用俄歇电子能谱(AES)研究了高真空下,环境温度对铀铌合金真空氧化膜的影响。
9·The influences of electrolyte components and preparation parameters on the film-forming process as well as properties of oxidation film were discussed.
对电解液中的各组分在成膜过程中的作用及电解工艺参数对成膜过程和膜层性能的影响进行了研究探讨。
10·Black oxidation film on aluminum alloy with good adhension, strong corrosion resistance and beautiful color can be obtained by two steps of oxidation coloring.
阶梯形铝器皿有二个优点:一是增加器皿的刚度; 二是经过阳极氧化着色之后阶梯越多越美观。