1·The flexural strength and flexural modulus decreased with the increasing amount of ABS.
合金的弯曲强度和弯曲模量都随着合金中abs用量的升高而下降。
2·Alkaline treatment of wood flour makes flexural strength and flexural modulus of the composite decrease by 20.
木粉的碱化处理使复合材料的弯曲强度和弯曲模量分别下降20。
3·The influence of hygrothermal environment on flexural strength of composites is greater than flexural modulus.
湿热对复合材料弯曲强度的影响要大于对弯曲模量的影响。
4·Experimental results show that the flexural modulus increases with the increases of the fibre content and length.
实验表明,随着纤维含有量和纤维长度的增加,材料弯曲模量呈递增趋势。
5·The results showed that the tensile strength, flexural strength and flexural modulus increased obviously with increase of amount of Mica.
结果表明,复合材料的拉伸强度、曲强度和弯曲模量随着云母用量的增加而提高。
6·The addition of OMMT improved the tensile strength, flexural strength and flexural modulus of the alloy, however, the impact strength decreased to a certain extent.
结果表明,OM MT的添加可以提高体系的拉伸强度、 弯曲强度和弯曲模量,但冲击强度会有某种程度的下降;
7·The results show that the addition of mica can enhance the flexural strength, flexural modulus, notched Izod impact strength and heat deformation temperature of the composites;
结果表明:云母可有效提高PP的弯曲强度及模量、悬臂梁缺口冲击强度和耐热性能;
8·Results showed that as the hardness of modified EPDM increased the brittle-ductile transition moved to high rubber contents and the flexural modulus increased profoundly, however.
结果表明:随着EPDM硬度的增加,共混物不仅韧性提高,弯曲模量也大幅度上升。
9·The result showed that impact strength of the blending system increased, while tensile strength, flexural strength and flexural modulus decreased with the addition of impact modifier ACR;
酯交换抑制剂的加入,降低了共混体系的力学性能,适当的酯交换反应有利于共混体系力学性能的提高;
10·It shows that after adding 20% low profile additive to the UP resin, the shrinkage rate of cured resin is 2.1%, the retention rate of bending strength is 88% and no change in flexural modulus.
结果表明,在不饱和聚酯树脂中加入2 0 %的该类低收缩添加剂,树脂的固化收缩率为2 1% , 弯曲强度保有率为88% ,弯由模量没有明显变化;