solution heat treatment

通过加热和保温
常用释义
溶液热处理:一种金属材料热处理工艺,通过加热和保温,使合金元素溶解在基体中,然后快速冷却,以获得均匀的固溶体组织。

例句

1·The results showed that natural ageing after solution heat treatment led to increase the comprehensive mechanical properties effectively.

通过固溶处理后自然时效,能有效地提高合金的综合力学性能。

2·The design methods, the structure characteristic, the composition and other problems of the Aluminum wheel hub solution heat treatment combined electric furnace were introduced.

介绍了铝轮毂固溶热处理联合电炉的设计方法、结构特点、炉子组成以及需要注意的问题。

3·Owing to the plastic deformation on the blade surface, recrystallization formed on the solid solution heat treatment. Before blade application, recrystallization zone existed already on its two sid…

叶片表面的再结晶在叶片使用之前就已存在,是由于固溶热处理前叶片的表面存在塑性变形,在固溶热处理过程中形成的。

4·The porous magnesium with different porosity was modified by alkali-heat-treatment and the samples were compared after soaked in the SBF solution.

采用碱热处理法对不同孔隙率的多孔镁表面进行改性,并将碱热处理处理后的试样置于SBF溶液中浸泡对比。

5·Applications: Used for the brazing, sintering and solution heat-treatment of automobile parts, stainless steel parts and powder metallurgical product.

用途:适用于汽车零部件、粉末冶金、不锈钢零件等的钎焊、烧结、固溶热处理工艺。

6·This paper is about construction and characteristics of C194, which are effected by heat-treatment of solution and aging .

研究了C194合金变形与固溶时效热处理工艺条件对其组织性能的影响。

7·Rhombohedral ITO solid solution was metastable in air and it would be transformed to cubic ITO solid solution by heat-treatment.

刚玉型结构ITO固溶体在空气中处于亚稳态,并且在加热的条件下可以转变为萤石型结构ITO固溶体。

8·Applications: Used for the brazing, sintering and solution heat-treatment of automobile parts, stainless steel parts and powder metallurgical products.

用途:适用于汽车零部件、粉末冶金、不锈钢零件等的钎焊、烧结、固溶热处理工艺。

9·The results indicate that natural ageing after solution heat-treatment leads to the effective increasement of the comprehensive mechnical properties.

通过固溶后自然时效处理,可有效地提高合金的综合力学性能;

10·Heat treatment methods, such as solid solution and quenching, have greatly enhanced its mechanical strength, which also leave a large internal residual stress in it.

固溶、淬火等热处理手段极大地提高了其机械强度,但同时使其内部产生了较大的残余应力。

同义词

[机]固溶热处理;固溶退火;均匀化