1·The results indicate that there is a coupled interface between alumina fiber and Si phase, and the fiber can serve as propitious sites for the heterogenous nucleation of Si phase.
结果表明氧化铝纤维与硅相之间存在共格界面,可作为硅相非自发形核的衬底;
2·Alumina fiber reinforced zinc alloy composites were manufactured by squeeze casting, and the effects of alumina fibers on the solidified structures of the zinc alloy composites were studied.
利用挤压铸造制备了氧化铝纤维增强锌合金复合材料,研究了氧化铝纤维对锌合金复合材料凝固组织的影响。
3·The experiment results have revealed as follows: 1) the catalytic activities of the Pt and Pd supported on the high alumina fiber of Huayan catalysts are higher than that supported on other fibers.
结果表明:利用淄博华岩耐火纤维公司生产的高铝型纤维棉作为载体制备的催化剂的活性最好;
4·The self-sharpening action of the cutting edge on the Fine Alumina Fiber Rod tips provides superior grinding performance. Continuous cutting edges provide stable and continuous grinding performance.
切削刃口可在加工过程中自行尖锐,以提供稳定而持续的研磨能力。
5·In this paper, the solidifying structure of alumina short fiber reinforced aluminum-silicon alloy composite is studied on the basis of domestic alumina short fibers.
本文在国产氧化铝短纤维基础上,研究了氧化铝短纤维增强铝硅合金复合材料的凝固组织。
6·The preparation method of alumina hollow fiber membrane by reaction bonding of aluminum oxide (RBAO) technique combined with dry wet spinning process was introduced in this paper.
介绍了铝氧化反应结合技术与干湿法纺丝工艺相结合制备氧化铝中空纤维膜的方法。
7·Types ASPA-1 and ASPA-2 alumina-silica fiber paper are premium grade lightweight refractory material made from high-purity alumina-silica fibers formed into highly flexible sheets.
ASPA - 1型和aspa - 2型的氧化铝—氧化硅纤维纸是优质的轻质耐火材料,它们由高纯度的氧化铝—氧化硅纤维制造成高弹性的薄片状的。